Neck turning question - Question on Lapua brass

[Varmint Hunter]

Am I going down a rabbit hole here with no returns? I'm not using this ammo in competition but rather in production made rifles for hunting. I do like to have very accurate ammo and will do what I can to make it as accurate as possible. I wasn't considering neck turning because of tight chambers in competition rifles. I was only seeking concentric brass and an equal amount of grab on the bullet all the way around. Was also hoping to reduce run out. I was thinking that the concentric brass would be more true coming out of the sizing dies. Especially if you were using bushing dies.

I wouldn't even consider turning brass for a production rifle. The chamber neck could already be very generous in diameter. Turning your case necks down would only increase the clearance which might not be helpful.

If you decide to turn some necks, only turn down 1/2 of them. This way you can try the same loads in turned and un-turned cases. Report back here with your findings.

It has also been discovered that brass with uneven neck wall thicknesses usually have uneven shoulder or body wall thicknesses, or so I have read. If that's the case, there isn't anything that can be done about those variances.

The easy button is to just buy quality brass. (but testing with a few cases won't hurt)

Good luck either way.

 

[MarkInPA]

I wouldn't even consider turning brass for a production rifle. The chamber neck could already be very generous in diameter. Turning your case necks down would only increase the clearance which might not be helpful.

If you decide to turn some necks, only turn down 1/2 of them. This way you can try the same loads in turned and un-turned cases. Report back here with your findings.

It has also been discovered that brass with uneven neck wall thicknesses usually have uneven shoulder or body wall thicknesses, or so I have read. If that's the case, there isn't anything that can be done about those variances.

The easy button is to just buy quality brass. (but testing with a few cases won't hurt)

G

"I wouldn't even consider turning brass for a production rifle. The chamber neck could already be very generous in diameter. Turning your case necks down would only increase the clearance which might not be helpful." Good point.

"If you decide to turn some necks, only turn down 1/2 of them. This way you can try the same loads in turned and un-turned cases. Report back here with your findings." Experiment for myself and find out what happens. Good idea.

" It has also been discovered that brass with uneven neck wall thicknesses usually have uneven shoulder or body wall thicknesses, or so I have read. If that's the case, there isn't anything that can be done about those variances." I've read that too. That's why I have one of these devices and use it.

This all sounds like good advice from someone who knows a thing or two. Thanks.

 

[Hard rock]

The best thing I ever did for eliminating run out and to improve concentric necks , is change to bushing dies with no expander and believe me I have tried everything . This does work best with LAPUA brass where no neck turning is necessary, for hunting loads , I get nearly 0 runout . I use to turn necks and never seen a gain with run of the mil brass win, rem etc.The only time it has become necessary is when necking down from a larger cal to a smaller cal and that would be from 30 cal to 6.5 or 25 cal ,or more.

 

[Coyote Shadow Tracker]

IMO might as well do a 100% percent clean up since you're already doing the work. but a skim turn is fine also. If your cutter matches the shoulder angle then by all means cut into the shoulder a little. It helps mitigate brass flow and possibly donuts.

View attachment 619435

YOU DA MAN!!!!!!!!!!!!
Love those necks.
We should talk some time
Len & Jill

 

[MagnumManiac]

This is how I have always prepped my necks for LR & ELR shooting.
My neck measurements are worked out FIRST on the brass I choose to use. Reamer print is then made. I aim for .003" clearance, including .0005" springback.
All of my brass necks are turned identically in each batch.
I only size 80%-85% of my neck length, I turn exactly to the end of this measurement and I only turn enough to give me the desired clearance and complete clean up.
I have the above Redding case neck gauge measuring set-up, absolute must-have for this, I also have other ball end mics, pin gauges and sized broaches, but you may not need them.
I found that 'cleaning up' necks for SAAMI chambers was a waste of time, so was measuring run-out, measuring CBTO and other precision oriented steps.
The clearances involved are just too large to matter…

If you 'feel' you get better accuracy or precision, then continue, but if you get passed all the noise by shooting 3 10 shot groups, your precision will most likely be average, just saying.

I do not neck turn on large SAAMI chambers, but if I find it necessary, I will skim turn to clean up 80% of the neck.
SAAMI hunting rifle chambers, unless 'Match', are too wish washy for precision loading, including those that CLAIM are precision…

Cheers.