Annealing is a function of TEMP and TIME. At 750 degrees Fahrenheit, it will take 1 hour for cartridge brass to properly anneal. That...

Buy one or make friends with someone that has one otherwise your just wasting your time

this is the one I got with the two torch set up love it will do 100 cases in no time at all. http://bench-source.com/id81.html

I did not build one,I just bought one and I do my brass every time I fire it and it works.

Do it in a dark room and you'll see the glow Annealing greatly benefits brass that is not uniform. If you have fresh...

The reason to anneal is not for case life, although this can be a side effect, it is for the sole reason to uniform neck tension, which...

That's what I got (750°), I've been practicing with hornady brass I'm willing to ruin. I still don't have the courage to try my lapua...

Split a good unit with several friends and you will never regret it. Especially the ones that analyze and give the CORRECT setting for...

There are 2 factors that HAVE to be adhered to, those are TEMPERATURE & TIME, either being wrong will affect the outcome. It is too...

Search YouTube for instructions by eric cortina(i think i got the name right).

I did this, he says go until there is a touch of red and then remove it. He did a test and cooked some way too long. He claims it didn't...

What's the temp of what one wants, the 750?

I'm going to build a case annealer, has doing this helped anyone's groups? I was thinking it might help with the odd flier, or make...